Conjugated porous polymers derived from diethynylarenes by chain-growth polymerization and polycyclotrimerization
Slováková, Eva ; Sedláček, Jan (advisor) ; Merna, Jan (referee) ; Červený, Libor (referee)
4 ABSTRACT The synthesis has been described yielding a new type of rigid conjugated polymer networks which possess a high content of permanent micropores and macropores and exhibit high surface areas up to 1469 m2/g. The networks have been prepared via chain-growth coordination polymerization catalysed with insertion catalysts based on Rh complexes. This polymerization has been newly applied to bifunctional acetylenic monomers of diethynylarene type (1,4-diethynylbenzene, 1,3-diethynylbenzene and 4,4'-diethynylbiphenyl). The covalent structure of the networks consists of the polyacetylene main chains densely connected by arylene struts. The W and Mo metathesis catalysts have been revealed as inefficient for the synthesis of these networks. The increase in the polymerization temperature and time has been shown to affect positively the content and the diameter (up to 22 nm) of the mesopores in the networks. A mechanism has been proposed that explains the mesopores formation as a result of mutual knitting of small particles of the microporous polymer. The application of emulsion polymerization technique allowed to prepare texturally hierarchical polyacetylene networks possessing interconnected open macropores (diameter up to 4,8 μm) the walls of which exhibited micro/mesoporous texture. It was demonstrated...
|
|
|
Conjugated porous polymers derived from diethynylarenes by chain-growth polymerization and polycyclotrimerization
Slováková, Eva
The synthesis has been described yielding a new type of rigid conjugated polymer networks which possess a high content of permanent micropores and macropores and exhibit high surface areas up to 1469 m2/g. The networks have been prepared via chain-growth coordination polymerization catalysed with insertion catalysts based on Rh complexes. This polymerization has been newly applied to bifunctional acetylenic monomers of diethynylarene type (1,4-diethynylbenzene, 1,3-diethynylbenzene and 4,4'-diethynylbiphenyl). The covalent structure of the networks consists of the polyacetylene main chains densely connected by arylene struts. The W and Mo metathesis catalysts have been revealed as inefficient for the synthesis of these networks. The increase in the polymerization temperature and time has been shown to affect positively the content and the diameter (up to 22 nm) of the mesopores in the networks. A mechanism has been proposed that explains the mesopores formation as a result of mutual knitting of small particles of the microporous polymer. The application of emulsion polymerization technique allowed to prepare texturally hierarchical polyacetylene networks possessing interconnected open macropores (diameter up to 4,8 μm) the walls of which exhibited micro/mesoporous texture. It was demonstrated that...
|
|
|
Conjugated porous polymers derived from diethynylarenes by chain-growth polymerization and polycyclotrimerization
Slováková, Eva ; Sedláček, Jan (advisor) ; Merna, Jan (referee) ; Červený, Libor (referee)
4 ABSTRACT The synthesis has been described yielding a new type of rigid conjugated polymer networks which possess a high content of permanent micropores and macropores and exhibit high surface areas up to 1469 m2/g. The networks have been prepared via chain-growth coordination polymerization catalysed with insertion catalysts based on Rh complexes. This polymerization has been newly applied to bifunctional acetylenic monomers of diethynylarene type (1,4-diethynylbenzene, 1,3-diethynylbenzene and 4,4'-diethynylbiphenyl). The covalent structure of the networks consists of the polyacetylene main chains densely connected by arylene struts. The W and Mo metathesis catalysts have been revealed as inefficient for the synthesis of these networks. The increase in the polymerization temperature and time has been shown to affect positively the content and the diameter (up to 22 nm) of the mesopores in the networks. A mechanism has been proposed that explains the mesopores formation as a result of mutual knitting of small particles of the microporous polymer. The application of emulsion polymerization technique allowed to prepare texturally hierarchical polyacetylene networks possessing interconnected open macropores (diameter up to 4,8 μm) the walls of which exhibited micro/mesoporous texture. It was demonstrated...
|
|
|
Polycyclotrimerization of alkynes with internal ethynyl groups
Sokol, Jiří ; Sedláček, Jan (advisor) ; Balcar, Hynek (referee)
The diynes of both aliphatic and aromatic types comprising either (i) two internal ethynyl groups or (ii) one internal and one terminal ethynyl group in the molecule were revealed as appropriate monomers for the Co2(CO)8 catalyzed polycyclotrimerization yielding high-molecular-weight products. The polycyclotrimerization of aliphatic diynes with a short (CH2)2 link between ethynyl groups and the polycyclotrimerization of aromatic diynes provided polycyclotrimer networks with tri-, tetra-, penta- and hexasubstituted benzene segments. The polycyclotrimers of aliphatic diynes did not exhibit microporous texture. On the other side, the polycyclotrimers of aromatic monomers were mostly microporous with specific surface area up to SBET = 499 m2 /g. The nitrogen desorption isotherms on microporous polycyclotrimers exhibited a significant unclosed hysteresis. This indicated that the penetration of nitrogen into polymers was accompanied by formation of temporary pores or opening permanent pores of worse accessibility.
|
|
|
Conjugated porous polymers derived from diethynylarenes by chain-growth polymerization and polycyclotrimerization
Slováková, Eva
The synthesis has been described yielding a new type of rigid conjugated polymer networks which possess a high content of permanent micropores and macropores and exhibit high surface areas up to 1469 m2/g. The networks have been prepared via chain-growth coordination polymerization catalysed with insertion catalysts based on Rh complexes. This polymerization has been newly applied to bifunctional acetylenic monomers of diethynylarene type (1,4-diethynylbenzene, 1,3-diethynylbenzene and 4,4'-diethynylbiphenyl). The covalent structure of the networks consists of the polyacetylene main chains densely connected by arylene struts. The W and Mo metathesis catalysts have been revealed as inefficient for the synthesis of these networks. The increase in the polymerization temperature and time has been shown to affect positively the content and the diameter (up to 22 nm) of the mesopores in the networks. A mechanism has been proposed that explains the mesopores formation as a result of mutual knitting of small particles of the microporous polymer. The application of emulsion polymerization technique allowed to prepare texturally hierarchical polyacetylene networks possessing interconnected open macropores (diameter up to 4,8 μm) the walls of which exhibited micro/mesoporous texture. It was demonstrated that...
|